塑胶原料 > 行业新闻 > 今日新到产品

Algoflon® F 6

Algoflon® F 6

2018-09-10 09:12:14

  

Algoflon® F 6      
Polytetrafluoroethylene      
Product Description:      
Algoflon® F 6 is a fine cut homopolymer PTFE powder that is white, granular and non-free flowing. It is designed for normal compression molding of rods and billets to obtain medium/large items and skived tapes (> 50 µm thick).
       
Algoflon® F 6 exhibits high bulk density, optimum isotropic behavior and very good mechanical and electrical properties.
       
Main features of Algoflon® F 6 are:      
       
Good isotropic properties      
       
Very good skivability      
       
Very good surface finishing      
       
Very good mechanical and electrical properties    
       
General  
Features  Good Chemical Resistance
Uses  Additive Blending  
Agency Ratings  FDA 21 CFR 177.1550
Appearance  White
Forms  Powder
Processing Method  Compression Molding

Physical Nominal Value Unit Test Method
Specific Gravity 2.17 　 ASTM D792
Average Particle Size 2 15 µm Internal Method
Bulk Density 380 g/l ASTM D4894
Shrinkage - Radial  3.2 % ASTM D4894
Mechanical Nominal Value Unit Test Method
Elongation at Break 370 % 　
Tensile Strength 42 MPa ASTM D4894
Electrical Nominal Value Unit Test Method
Dielectric Strength 65 kV/mm ASTM D149
Additional Information
Processing
Algoflon® F 6 is processed according to methods generally used for normal compression molding. Prior to use, the powder must be conditioned above 19°C/66°F.
The processing involves typically two steps: preforming and sintering. Initially the powder is compacted into a preform. This is then sintered using precise sintering (heating and cooling) cycle to take the temperature above the PTFE crystalline melting point to attain the final article. The preforming pressure, dwell time at maximum sintering temperature and cooling rate are all established according to the shape and size of the final item.
Storage and Handling
Algoflon® PTFE fine cut powders must be stored and handled carefully to achieve defect-free molding. Before use the temperature of the powder must be conditioned above 19°C/66°F (between 21-27°C/70-81°F). Below this temperature the powder is difficult to mold without cracks. Temperatures that are too high should also be avoided to prevent powder lumping and poor flow.
Storage and handling facilities should be clean since even very small foreign particles can cause defects in finished products. Keep resin drums closed and clean. Good housekeeping and careful handling are essential.
Safety and Toxicology
Before using Algoflon® PTFE fine cut powders, consult the product Material Safety Data Sheet and follow all label directions and handling precautions.
As with all PTFE materials, handling and processing should only be carried out in well ventilated areas. Vapor extractor units should be installed above processing equipment. Fumes must not be inhaled and eye and skin contact ought to be avoided. In case of skin contact, wash with soap and water. In case of eye contact, flush with water immediately and seek medical help.
Do not smoke in areas contaminated with powder, vapor or fumes.
See Material Safety Data Sheet for detailed advice on waste disposal methods.
Packaging
Algoflon® F 6 is packaged in 25 kg nonreturnable drums. Each drum contains two bag liners made of polyethylene resin.