| Teflon® PTFE 7A X | |||
| Polytetrafluoroethylene | |||
| Product Description: | |||
| Teflon ® PTFE 7A X is a white powder with small particle size and high bulk density. The small particle size of Teflon ® PTFE 7A X helps to minimize voids even at relatively low molding pressures. High bulk density increases the size of moldings possible from a given mold or press opening. Teflon ® PTFE 7A X is preferred for large moldings, such as billets, requiring optimum mechanical and electrical properties. It is also used in a mixture with fillers when they are added to modify the mechanical properties of moldings. Properly processed products made from neat Teflon ®PTFE 7A X provide the superior properties typical of the fluoroplastic resins: retention of properties after service at 260 °C (500 °F), useful properties at -240 °C (-400 °F), chemical inertness to nearly all industrial chemicals and solvents, and low friction and anti-stick surfaces. Dielectric properties are outstanding and stable with frequency and temperature. Molded products have moderate stiffness and high elongation. | |||
| Teflon ® PTFE 7A X resists ignition and does not promote flame | |||
| spread. When ignited by flame from other sources, the contribution of heat is small and with little smoke. Statements, or data, regarding behavior in a flame situation are not intended to reflect hazards presented by this or any other material when under actual fire conditions. | |||
| Typical Applications | |||
| Many end products are fabricated from moldings of Teflon ® PTFE 7A X, including skived film and sheet, gaskets, packings, mechanical seals, bridge or pipeline bearing pads, shaft bearings, electrical insulators, piston rings, expansion bellows, diaphragms, and chemical linings. The use of fillers provides a wide choice of modified mechanical properties. | |||
| General | |||
| Europe | North America | ||
| Features | Food Contact Acceptable | High Elongation | Solvent Resistant |
| Good Chemical Resistance | Low Friction | ||
| Good Stiffness | Low Smoke Emission | ||
| Uses | Bearings | Film | Sealing Devices |
| Diaphragms | Gaskets | Seals | |
| Electronic Insulation | Liners | Sheet | |
| Agency Ratings | FDA 21 CFR 177.1550 | ||
| Appearance | White | ||
| Forms | Powder | ||
| Processing Method | Compression Molding | Sintering | |
| Physical | Nominal Value | Unit | Test Method |
| Specific Gravity | 2.15 | g/cm³ | ASTM D4894, ISO 12086 |
| Apparent Density | 0.46 | g/cm³ | ASTM D4894, ISO 12086 |
| Average Particle Size | |||
| -- | 34 | µm | ISO 13320 |
| -- | 34 | µm | ASTM D4894 |
| Water Content | |||
| -- | < 0.040 | % | ISO 12086 |
| -- | < 0.040 | % | ASTM D4894 |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Strength (0.130 mm) | 34.5 | MPa | ASTM D4894, ISO 12086 |
| Tensile Elongation (Break, 0.130 mm) | 380 | % | ASTM D4894, ISO 12086 |
| Thermal | Nominal Value | Unit | Test Method |
| Melting Temperature | ISO 12086, ASTM D4894 | ||
| -- 3 | 317 to 337 | °C | |
| -- 4 | 334 to 354 | °C | |
| Thermal Instability Index | |||
| -- | < 3.00 | ISO 12086 | |
| -- | < 3.00 | ASTM D4894 |