3M™ Dyneon™ TFM™ Modified PTFE Compound 6105 BR

2018-09-08 17:57:13

3M™ Dyneon™ TFM™ Modified PTFE Compound 6105 BR
Polytetrafluoroethylene
25% Glass Fiber
Product Description:
3M™ Dyneon™ TFM™ Modified PTFE Compound 6105 BR is a Polytetrafluoroethylene (PTFE) product filled with 25% glass fiber. It can be processed by compression molding or sintering and is available in Europe or North America.


General
Filler / Reinforcement	Glass Fiber, 25% Filler by Weight

Features	Good Flow

Appearance	Brown

Processing Method	Compression Molding	Sintering

Physical	Nominal Value	Unit	Test Method
Specific Gravity	2.2	g/cm³	ASTM D4745-06
Apparent Density	0.94	g/cm³	ASTM D4894
Molding Shrinkage - Flow	2.2	%	ASTM D4894-07
Hardness	Nominal Value	Unit	Test Method
Shore Hardness² (Shore D)	68		DIN 53505
Mechanical	Nominal Value	Unit	Test Method
Tensile Strength² (Break)	14.6	MPa	ASTM D4745-06
Tensile Elongation² (Break)	370	%	ASTM D4745-06
Additional Information	Nominal Value	Unit
Compression Molding Molding Pressure	60	MPa
Compression Molding Temperature	23 to 26	°C
Sintering Temperature	< 365	°C

3M&#8482; Dyneon&#8482; TFM&#8482; Modified PTFE Compound 6105 BR