| 3M™ Dyneon™ TFM™ Modified PTFE Compound 4105 | |||
| Polytetrafluoroethylene | |||
| 25% Glass Fiber | |||
| Product Description: | |||
| 3M™ Dyneon™ TFM™ Modified PTFE Compound 4105 is a Polytetrafluoroethylene (PTFE) product filled with 25% glass fiber. It can be processed by compression molding or sintering and is available in Europe or North America. Typical application: Engineering/Industrial Parts. | |||
| General | |||
| Filler / Reinforcement | Glass Fiber, 25% Filler by Weight | ||
| Features | Good Flow | ||
| Uses | Bearings | Valves/Valve Parts | |
| Processing Method | Compression Molding | Sintering | |
| Physical | Nominal Value | Unit | Test Method |
| Density | 2.24 | g/cm³ | ISO 12086 |
| Apparent Density | 0.82 | g/cm³ | ISO 12086 |
| Average Particle Size | 580 | µm | ISO 12086 |
| Mechanical | Nominal Value | Unit | Test Method |
| Deformation Under Load 2 (23°C, 15 MPa) | 3.50 | % | ASTM D621 |
| Films | Nominal Value | Unit | Test Method |
| Tensile Strength - TD 3 (1000 µm) | 14.0 | MPa | ISO 12086 |
| Tensile Elongation - TD 3 (Break, 1000 µm) | 420 | % | ISO 12086 |
| Additional Information | Nominal Value | Unit | |
| Compression Molding Molding Pressure | 70.0 | MPa | |
| Compression Molding Temperature | 23 to 26 | °C | |
| Sintering Temperature | 370 to 375 | °C |