| 3M™ Dyneon™ PTFE Compound TF 6711 | |||
| Polytetrafluoroethylene | |||
| 5.0% Glass Fiber | |||
| Product Description: | |||
| Features | |||
| PTFE Compound with 5% glass fibre and 5% molybdenumdisulfide | |||
| Free flow compound | |||
| General | |||
| Filler / Reinforcement | Glass Fiber, 5.0% Filler by Weight | ||
| Additive | Molybdenum Disulfide Lubricant (5%) | ||
| Features | Good Flow | Lubricated | |
| Processing Method | Compression Molding | Sintering | |
| Physical | Nominal Value | Unit | Test Method |
| Specific Gravity | 2.25 | g/cm³ | ASTM D4745-06 |
| Apparent Density | 0.75 | g/cm³ | ASTM D4894-07 |
| Molding Shrinkage - Flow | 2.1 | % | ASTM D4894-07 |
| Hardness | Nominal Value | Unit | Test Method |
| Shore Hardness 2 (Shore D) | 67 | DIN 53505 | |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Strength 2 (Break) | 24 | MPa | ASTM D4745-06 |
| Tensile Elongation 2 (Break) | 300 | % | ASTM D4745-06 |
| Additional Information | Nominal Value | Unit | |
| Compression Molding Molding Pressure | 50 | MPa | |
| Compression Molding Temperature | 23 to 26 | °C | |
| Sintering Temperature | < 365 | °C |