| 3M™ Dyneon™ PTFE Compound TF 6302 | |||
| Polytetrafluoroethylene | |||
| 10% Graphite Fiber | |||
| Product Description: | |||
| Features | |||
| PTFE Compound with 10 % graphite | |||
| Free flow compound | |||
| General | |||
| Filler / Reinforcement | Graphite Fiber, 10% Filler by Weight | ||
| Features | Good Flow | ||
| Processing Method | Compression Molding | Sintering | |
Physical
Nominal Value
Unit
Test Method
Specific Gravity
2.15
g/cm³
ASTM D4745-06
Apparent Density
0.75
g/cm³
ASTM D4894-07
Molding Shrinkage - Flow
2.2
%
ASTM D4894-07
Hardness
Nominal Value
Unit
Test Method
Shore Hardness 2 (Shore D)
68
DIN 53505
Mechanical
Nominal Value
Unit
Test Method
Tensile Strength 2 (Break)
26.2
MPa
ASTM D4745-06
Tensile Elongation 2 (Break)
320
%
ASTM D4745-06
Additional Information
Nominal Value
Unit
Compression Molding Molding Pressure
50
MPa
Compression Molding Temperature
23 to 26
°C
Sintering Temperature
< 365
°C