3M™ Dyneon™ PTFE Compound TF 6105-N

2018-09-08 17:55:25

3M™ Dyneon™ PTFE Compound TF 6105-N
Polytetrafluoroethylene
25% Glass Fiber
Product Description:
Features

Dyneon™ PTFE Compound with 25 % glass fibre

Free flow compound

General
Filler / Reinforcement	Glass Fiber, 25% Filler by Weight
Filler / Reinforcement	Glass Fiber, 25% Filler by Weight
Features	Good Flow
Features	Good Flow
Processing Method	Compression Molding	Sintering
Processing Method	Compression Molding	Sintering

Physical	Nominal Value	Unit	Test Method
Specific Gravity	2.18	g/cm³	ASTM D4745-06
Apparent Density	0.81	g/cm³	ASTM D4894-07
Molding Shrinkage - Flow	1.4	%	ASTM D4894-07
Hardness	Nominal Value	Unit	Test Method
Shore Hardness² (Shore D)	67		DIN 53505
Mechanical	Nominal Value	Unit	Test Method
Tensile Strength² (Break)	15.5	MPa	ASTM D4745-06
Tensile Elongation² (Break)	300	%	ASTM D4745-06
Additional Information	Nominal Value	Unit
Compression Molding Molding Pressure	60	MPa
Compression Molding Temperature	23 to 26	°C
Sintering Temperature	< 365	°C

²Measured on sintered moldings

3M&#8482; Dyneon&#8482; PTFE Compound TF 6105-N