| 3M™ Dyneon™ PTFE Compound TF 4216 | |||
| Polytetrafluoroethylene | |||
| 33% Carbon Fiber | |||
| Product Description: | |||
| Features | |||
| Dyneon™ PTFE Compound with 33 % electrographitized carbon | |||
| Free flow compound | |||
| General | |||
| Filler / Reinforcement | Carbon Fiber, 33% Filler by Weight | ||
| Features | Good Flow | ||
| Processing Method | Compression Molding | Sintering | |
| Physical | Nominal Value | Unit | Test Method |
| Specific Gravity | 2.09 | g/cm³ | ASTM D4745-06 |
| Apparent Density | 0.69 | g/cm³ | ASTM D4894-07 |
| Molding Shrinkage - Flow | 1.9 | % | ASTM D4894-07 |
| Hardness | Nominal Value | Unit | Test Method |
| Shore Hardness 2 (Shore D) | 62 | DIN 53505 | |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Strength 2 (Break) | 14.5 | MPa | ASTM D4745-06 |
| Tensile Elongation 2 (Break) | 70 | % | ASTM D4745-06 |
| Additional Information | Nominal Value | Unit | |
| Compression Molding Molding Pressure | 90 | MPa | |
| Compression Molding Temperature | 23 to 26 | °C | |
| Sintering Temperature | < 365 | °C | |
| 2Measured on sintered moldings |