3M™ Dyneon™ PTFE Compound TF 4104

2018-09-08 17:56:12

3M™ Dyneon™ PTFE Compound TF 4104
Polytetrafluoroethylene
20% Glass Fiber
Product Description:
Features

PTFE Compound with 20 % glass fibre

Free flow compound

Typical applications:

Valve seats

Piston rings

Bearings


General
Filler / Reinforcement	Glass Fiber, 20% Filler by Weight
Filler / Reinforcement	Glass Fiber, 20% Filler by Weight
Features	Good Flow
Features	Good Flow
Uses	Bearings	Valves/Valve Parts
Uses	Bearings	Valves/Valve Parts
Processing Method	Compression Molding	Sintering
Processing Method	Compression Molding	Sintering

Physical	Nominal Value	Unit	Test Method
Density	2.22	g/cm³	ISO 12086
Apparent Density	0.82	g/cm³	ISO 12086
Average Particle Size	580	µm	ISO 12086
Mechanical	Nominal Value	Unit	Test Method
Tensile Stress² (Break)	18	MPa	ISO 12086
Tensile Strain² (Break)	390	%	ISO 12086
Deformation Under Load³ (23°C, 15 MPa)	8.5	%	ASTM D621
Additional Information	Nominal Value	Unit
Compression Molding Molding Pressure	60	MPa
Compression Molding Temperature	23 to 26	°C
Sintering Temperature	< 365	°C

²Measured on sintered moldings
³100 h load, 25 h relaxation