OXPEKK® IG200

2023-02-27

OXPEKK® IG200
Polyetherketoneketone
Product Description
OXPEKK® IG200 is a Polyetherketoneketone (PEKK) material. It is available in Europe or North America for injection molding. Primary attribute of OXPEKK® IG200: Crystalline.

Typical application of OXPEKK® IG200: Medical/Healthcare
General
Features	Crystalline

Uses	Body Implants

Forms	Pellets

Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.31	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (400°C/8.4 kg)	100 to 120	g/10 min	ASTM D1238
Molding Shrinkage - Flow	1.4	%	ASTM D955
Water Absorption (24 hr)	< 0.20	%	ASTM D570
Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	88		ASTM D785
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	4410	MPa	ASTM D638
Tensile Strength			ASTM D638
Yield	138	MPa
Break	110	MPa
Tensile Elongation			ASTM D638
Yield	4.0	%
Break	12	%
Flexural Modulus	4550	MPa	ASTM D790
Flexural Strength (5.0% Strain)	193	MPa	ASTM D790
Compressive Strength	207	MPa	ASTM D695
Shear Strength	138	MPa	ASTM D732
Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	53	J/m	ASTM D256
Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	175	°C	ASTM D648
Glass Transition Temperature	163	°C	DSC
Melting Temperature	360	°C	DSC
CLTE - Flow	2.1E-5	cm/cm/°C	ASTM D696